THE POSITION OF THE JOINTS WITH ANGLE OF 900 AT FRICTION STIR WELDING (FSW)

Abstract

This research was use aluminum 6061 with 150 mm length, 50 mm wide, and 10 mm thick. The probe was made from EMS 45 simple design. Three variations used of feedrate speed  is 10 mm/min, 15 mm/min, and 30 mm/min. Spindle rotation constantly set 2000 rpm, the heat generated was recorded. Corner-Butt (C-B)joint determined, the lowest heat generated from 2200C-3200C and the tensile test was60 MPa. The highest tensile testwas 163 MPa, achieved by Corner-butt 45 (C-B 45) joint on 10 mm/min feedrate speed. It was verified by the heat temperature from 3000C-4200C and clarified by its micro and macrostructure.

Recommended articles

ANALYSIS OF TURNING MOTION FOR DEVELOPING A BUTTERFLY-STYLE FLAPPING ROBOT

YUTA OZAWA, TARO FUJIKAWA, KOKI KIKUCHI
Keywords: small flapping robot | butterfly | turning flight | asymmetric wings | swept-forward angle | rotational direction of an actuator

AIR COATED ABRASIVE SUSPENSION JETS UNDER SUBMERGED CONDITION

SEIJI SHIMIZU, GUOYI PENG, YASUYUKI OGUMA
Keywords: abrasive suspension jet | submerged cutting | air coated jet | high-speed observation | pulsation

MECHANICAL PROPERTIES OF LOW DENSITY POLYETHYLENE (LDPE) IRRADIATED BY LOW DOSES BETA IRRADIATION MEASUREMENT BY ULTRA NANOINDENATION TEST

TOMAS FIALA, DAVID MANAS, MIROSLAV MANAS, LENKA GAJZLEROVA
Keywords: low density polyethylene (LDPE) | cross-linking | ultranano-hardness | surface layer

THE MODERN STORAGE EQUIPMENT WITH EMPHASIS ON INNOVATIONS AND RISKS

VERA PELANTOVA, EVA SIROVA
Keywords: storage equipment | store | automation | innovation | risk | industry 4.0 | organisation